고로 서냉슬래그 혼합 시멘트 페이스트의 유동성

Journal of the Korea Concrete Institute, 2012

Cement has been traditionally used as a main binding material of high ductile fiber reinforced cementitious composites. The purpose of this paper is to investigate the feasibility of using alkali-activated slag and polyvinyl alcohol (PVA) fibers for manufacturing high ductile fiber reinforced cementless composites. Two mixture proportions with proper flowability and mortar viscosity for easy fiber mixing and uniform fiber dispersion were selected based on alkali activators. Then, the slump flow, compression, uniaxial tension and bending tests were performed on the mixes to evaluate the basic properties of the composites. The cementless composites showed an average slump flow of 465 mm and tensile strain capacity of approximately 2% of due to formation of multiple micro-cracks. Test results demonstrated a feasibility of manufacturing high ductile fiber reinforced composites without using cement.

Clean Technology, 2014

General household vacuum cleaners consist of dust collector, pre filter, motor and exhaust filter, and the filtered clean air is discharged to the atmosphere. By using the CFD methods, we estimated the internal flow in two types of commercial cyclone vacuum cleaners to evaluate the dust collection performance. From the analysis, it was known that the number of revolution had higher values in cyclone cone region. CFD analysis in a specific showed non-uniform velocity distribution at outlet, which results in the deterioration of particle collection performance. In order to improve flow condition, the installation of baffle was proposed and the values of velocity RMS were estimated.

Journal of the Korea Foundry Society, 2011

Journal of the Korean Institute of Building Construction, 2019

As a cold-weather-concrete construction technique for enhancing the sustainability and improving efficiency of cold-weather construction, the cracking timing, the starting point of deterioration for concrete, due to the shrinkage of the blast furnace slag cement concrete including accelerator was evaluated. As a result, by using blast furnace slag and accelerator, the cracking was developed faster with higher cracking potential under the restrained conditions at constant age and free-shrinkage strain. It can be considered that the results of decreased stress relaxation by creep or increased restraint with increased free-shrinkage strain causes the increased cracking development speed. Hence, it should be considered the necessary of cracking due to the shrinkage when blast furnace slag or accelerator was used for cold-weather construction.

Journal of the Korean Ceramic Society, 2012

Silicon carbide(SiC) exhibits many unique properties, such as high strength, corrosion resistance, and high temperature stability. In this study, a SiC-fiber web was prepared from polycarbosilane(PCS) solution by employing the electrospinning process. Then, the SiCfiber web was pyrolyzed at 1800 o C in argon atmosphere after it was subjected to a thermal curing. The SiC-fiber web (ground web)/ phenolic resin (resol) composite was fabricated by hot pressing after mixing the SiC-fiber web and the phenolic resin. The SiC-fiber web composition was controlled by changing the fraction of filler (filler/binder = 9:1, 8:2, 7:3, 6:4, 5:5). Thermal conductivity measurement indicates that at the filler content of 60%, the thermal conductivity was highest, at 6.6 W/mK, due to the resulting structure formed by the filler and binder being closed-packed. Finally, the microstructure of the composites of SiC-fiber web/resin was investigated by FE-SEM, EDS, and XRD.

KSCE Journal of Civil and Environmental Engineering Research, 2011

A series of field and laboratory permeability tests were performed to investigate the pore-clogging phenomenon of porous concrete used for pavement materials of a road. The field permeability tests were conducted for 37 study points in Jeju city, using the porous concretes with 13mm of maximum coarse aggregate (G max ). The results show that the service life of porous concrete is about 22 months when the permeability of the porous concrete is designed for 0.01 cm/sec. Some specimens were made with the purpose of recreating pore-clogging phenomenon. Tests were done for injected concentration of pore-clogging materials or size of maximum coarse aggregates (G max ). The test results demonstrated that relatively long in service life experienced with small amount of injected concentration of pore-clogging materials, whereas relatively short in service life experienced with a reduction in size of maximum coarse aggregates (G max ). In conclusion, the service life of porous concrete is in proportion to the concentration of pore-clogging material but it is in inverse proportion to the size of maximum coarse aggregate (G max ). Thus, the persisting period of porous concrete can be determined with respect to concentration of pore-clogging materials or size of maximum coarse aggregates (G max ).

Journal of the Korea Academia-Industrial cooperation Society, 2011

The core of IT products, electronic components, especially the MLCC, chip inductors, chip Varistors and so on. In order to test the electrical characteristics of the chip using the Reno-pin contact test method has been used. In current chips, mass production of semiconductor manufacturing processes, high-speed production test for the chip speed up, precision is required. But Vibration displacement is a very short, so in order to overcome these shortcomings, the displacement amplification to design the structure has been actively studied. In this paper, a building structure with a flexible hinge was designed amplification instrument, semiconductor chip industry in the performance test and inspection equipment to measure the electrical characteristics of high speed linear actuators Reno-Pin using system was developed.

Journal of the Korea Concrete Institute, 2009

Mechanical properties of steel-concrete interface were evaluated on the basis of experimental observations. The properties included bond strength, unbounded and bonded friction angles, residual level of friction angle, mode I fracture energy, mode II bonded fracture energy and unbonded slip-friction energy under different levels of normal stress, and shape parameters to define geometrical shape of failure envelope. For this purpose, a typical type of constitutive model of describing steel-concrete interface behavior was presented based on a hyperbolic three-parameter Mohr-Coulomb type failure criterion. The constitutive model depicts the strong dependency of interface behavior on bonding condition of interface, bonded or unbounded. Values of the interface parameters were determined through interpretation of experimental results, geometry of failure envelope and sensitivity analysis. Nonlinear finite element analysis that incorporates steel-concrete interface as well as material nonlinearities of concrete and steel were performed to predict the experimental results.

Journal of Korean navigation and port research, 2006

Transactions of the KSME C: Industrial Technology and Innovation, 2015

In this study, the finite element analysis was carried out to investigate dynamic characteristics of the AGF(Active Gurney Flap) which is under development for reducing vibration and noise of the helicopter rotor system. The Gurney flap is a kind of small flat plate, mounted normal to the lower surface of the airfoil near to the trailing edge. An electric motor, L-shaped linkages and flap parts were integrated into a rotor bade, and 3~5/rev control was given to the AGF to reduce the vibration in the fixed frame. Thus, an explicit time integration method was adopted to investigate the dynamic response of the AGF with considering both centrifugal force due to the rotor rotation and active control input, and it can be seen that the vertical displacement of the AGF was satisfied to meet the design requirement.