In the method for producing a copper-titanium-hydrogen alloy, a copper-titanium alloy in which titanium of 1 to 7.5 atom% is made to enter into a solid solution is rapidly cooled, the obtained supersaturated solid solution copper-titanium alloy is cold-rolled, and is thereafter subjected to age precipitation hardening, and also, hydrogen is incorporated therein.例文帳に追加

１ａｔ％以上、７．５ａｔ％以下のチタンを固溶させた銅−チタン合金を急冷し、得られた過飽和固溶体銅−チタン合金を冷間圧延した後、時効析出硬化させ、かつ水素を含有させる、銅−チタン−水素合金の製造方法が提供される。 - 特許庁

A conductor paste containing a powder of a tin particle and a tin-bismuth powder is filled between a first conductive material 21a and a second conductive material 24a, wherein the tin particle contains a supersaturated solid solution of copper in the particle.例文帳に追加

第１導電材２１ａおよび第２導電材２４ａの間に、粒子中に過飽和固溶した銅を含む錫粒子の粉末、および、錫ビスマス粉末を含む導体ペーストを充填する。 - 特許庁

This manufacturing method includes subjecting a composite wire rod consisting of an Al alloy containing more Si and Ge than the solid solubility limit in the equilibrium state and Nb, to rapid heating and quenching treatment in the state of the composite wire rod, to change an Al alloy core into a supersaturated solid solution.例文帳に追加

ＡｌにＳｉ、Ｇｅ等を平衡状態の固溶限を越えて添加した合金とＮｂとの複合線材において、複合線材のままの状態で急熱急冷処理することにより、Ａｌ合金芯を過飽和の固溶体に変える。 - 特許庁

A corrosion protective film 2 to be formed on the surface of the iron base 1 of a cast iron tube is formed of an aluminum alloy having a composition containing, by mass, 5 to 25% manganese, and the balance aluminum, and in which manganese is entered into solid solution in an aluminum phase in a supersaturated way.例文帳に追加

鋳鉄管の鉄素地１の表面に形成される防食皮膜２が、マンガンを５質量％以上かつ２５質量％以下含みかつ残部がアルミニウムであって、アルミニウム相にマンガンが過飽和に固溶されたアルミニウム合金にて形成される。 - 特許庁

An Al alloy solidified material, having a composition represented by general formula AlbalTia (where (a) satisfies 0<a≤20 in atomic %) and also having a structure composed essentially of supersaturated solid solution phase, is subjected to heat treatment or/and hot plastic working at 250-450°C.例文帳に追加

一般式：Ａｌ_balＴｉ_a（ただし、ａは原子パーセントで０＜ａ≦２０）で示される組成からなり、実質的に組織が過飽和固溶体相からなるＡｌ合金固化材を温度２５０〜４５０℃の範囲で熱処理又は／及び熱間塑性加工を施す方法である。 - 特許庁

Further, a rapidly cooled aluminum alloy having a composition containing 5 to 25% manganese, and the balance aluminum, and in which manganese is entered into solid solution in an aluminum phase in a supersaturated way is thermally sprayed on the surface of the iron base 1 of a cast iron tube to form a corrosion protective film 2 having a thickness of 50 to 200 μm on the surface of the iron base 1.例文帳に追加

また、マンガンをを５質量％以上かつ２５質量％以下含みかつ残部がアルミニウムであるとともに、アルミニウム相にマンガンが過飽和に固溶された急冷アルミニウム合金を鋳鉄管の鉄素地１の表面に溶射して、この鉄素地１の表面に、厚さが５０μｍ以上かつ２００μｍ以下の防食皮膜２を形成する。 - 特許庁