rupture zoneとは 意味・読み方・使い方

OPTIMIZATION METHOD FOR INTENSIFYING RUPTURE STRENGTH IN SPOT WELD ZONE例文帳に追加

スポット溶接部の破断強度増大のための最適化方法 - 特許庁

To prevent the rupture of a spot weld zone during impact of an arbitrary member, to optimize a deformation buckling mode, and to improve the absorption of impact energy by calculating one or more kinds of the width, board thickness, material strength and a nugget diameter of the spot weld zone to maximize the rupture strength in the weld zone of the member during impact deformation.例文帳に追加

衝撃変形時に任意の部材のスポット溶接部における破断強度を最大にする幅、板厚、材料強度、スポット溶接部のナゲット径のうち１種以上を算出し、部材の衝撃時の溶接部破断を防ぎ、変形座屈モードの適正化を図り、衝撃エネルギーの吸収を向上させる。 - 特許庁

To provide a method for ensuring rupture of the sliver in a structurally simple manner, draft is increased in a draft zone b arranged at the front stage of a sliver outlet to initiate the can replacement when a thin sliver location 12' is provided in a deposited sliver and the thin sliver location is about to the outlet zone of the sliver outlet of a coiler plate.例文帳に追加

設計上簡単な仕方でスライバの確実な切断を可能にする方法を提供するために、重合スライバ内に薄肉部12′が生じてこの薄肉部がコイラプレートのスライバ排出口の出口区域に来たときにケンス交換が開始するように、スライバ排出口の前段に配置されたドラフトゾーンｂでドラフトを増す。 - 特許庁

To make the creep rupture strength of a welding heat affected zone be hardly reduced, and to achieve long lifetime when the welded part structure of austenitic high-Ni steel products containing, by mass, 20-45% Cr is used for a long period of time at the temperature of ≥1,000°C.例文帳に追加

質量％で、Ｃｒ：２０〜４５％を含有するオーステナイト系高Ｎｉ鋼材同士の溶接接合部構造において、１０００℃以上の温度で長期間使用したとき、溶接熱影響部のクリープ破断強度が低下し難く、長寿命を達成する。 - 特許庁

To improve the quality of final products and the surface finish thereof by providing a device in a reheating zone of an induction heating device, which can prevent the formation of extra-rupture electric arcs between a steel product and a roller supporting the steel product.例文帳に追加

誘導加熱装置の再加熱領域において、鋼製品とその製品を支持するローラーの間に過遮断電気アークが出現することを防止できる装置を設けることにより、このような不利を軽減し、それによって最終製品の品質および表面仕上げ状態を改善すること。 - 特許庁