refractory stageとは 意味・読み方・使い方

To reduce the cost required for burying waste by providing a two stage lateral blow tuyere between a waste loading opening and a molten slag discharge opening and moving the blowing forward end part ofone tuyere in the horizontal direction between the core and lining refractory.例文帳に追加

廃棄物を高温でガス化溶融する際に問題となる内張り耐火物および羽口先端の損耗とを抑制して、経済的に処理できる方法を提供する。 - 特許庁

To provide highly durable magnesia-carbon type refractory which can suppress structural degradation under a use environment being exposed in high temperature surroundings for a long period of time, thereby maintain corrosion resistance in the initial stage of use.例文帳に追加

本発明は、長期間高温環境下に曝される様な使用環境下において、組織劣化を抑制でき、使用初期の耐食性を維持可能な高耐用性のマグネシア−カーボン質耐火物を提供することを目的とする。 - 特許庁

Molten metal is charged and discharged two or more times, after changing the lining of refractory layer of a molten metal vessel 2, and the shape of inner surface 21 of the vessel 2 is measured at the stage when the thermal deformation of the vessel 2 has converged to obtain a reference value.例文帳に追加

溶融金属用容器２の耐火物層を張り替えた後、溶融金属の収容、排出を複数回行って、容器２の熱変形が収束した段階における容器２の内面２１形状を計測して基準値とする。 - 特許庁

To solve the problem that a recast part produced when a core pattern is laser-cut from a refractory metal-based sheet in a core forming stage according to an investment casting process causes cracks, so as to cause defects in the dimensional precision of the cast hollow components.例文帳に追加

インベストメント鋳造法におけるコア形成工程で耐火金属ベースの金属板からコア原型をレーザ切断する際に生じるリキャスト（ｒｅｃａｓｔ）部分は、亀裂の原因となり、鋳造された中空コンポーネントの寸法精度に欠陥を生じさせる。 - 特許庁

In the case that the long time continuous casting is executed, the treatment by a ladle at a secondary refining stage prior to the continuous casting is performed for a time longer than that required for making the temperature of the refractory in the internal wall of the ladle to be almost stabilized, and making the heat radiation amount from the ladle to be stabilized.例文帳に追加

長時間の連続鋳造を行うに当たり、この連続鋳造に先立つ取鍋での二次精錬段階での処理を、その取鍋内壁耐火物の温度がほぼ安定化し、取鍋からの放熱量が定常化する時間以上行う。 - 特許庁

To provide a cooling roll and a twin roll type continuous casting method which enable, in the initial stage of casting, quick formation of good sealing state and after coming into a stationary state of casting, maintaining of the good sealing state by making a side weir refractory wear by necessary amount at the necessary time.例文帳に追加

鋳造初期には、速やかに良好なシール状態を形成し、鋳造が定常状態に至った後は、必要な時に必要量サイド堰耐火物を摩耗せしめ、良好なシール状態を維持する冷却ドラムと双ドラム式連続鋳造方法を提供する。 - 特許庁

To obtain a sealing material satisfactory fluidized at ≤530°C and further hard to be deformed in an evacuation stage at 450 to 500°C, so as to improve the characteristics of a PDP (plasma display panel) or the like and production efficiency in a sealing material comprising bismuth based glass powder and refractory filler powder.例文帳に追加

本発明は、ビスマス系ガラス粉末と耐火性フィラー粉末を含有する封着材料において、５３０℃以下の温度で良好に流動するとともに、４５０〜５００℃の真空排気工程で変形し難い封着材料を得ることにより、ＰＤＰ等の特性および製造効率を向上させることを技術的課題とする。 - 特許庁

At this time, preferably, the molten metal of ferrochromium is produced by the remelting of undersize products produced in a crushing stage for a ferrochromium product, the molten metal of ferrochromium is heated to 1,680°C or more, and the molten metal of ferrochromium is stored in a vessel lined by a carbonaseous refractory, and flux without substantially containing SiO2 is added to the inside of the vessel.例文帳に追加

その際に、前記フェロクロム溶湯をフェロクロム製品の破砕工程で発生する篩下品の再溶解により製造すること、前記フェロクロム溶湯を１６８０℃以上まで加熱すること、及び、前記フェロクロム溶湯を炭素質系の耐火物でライニングされた容器内に収容し、この容器内には実質的にＳｉＯ_2 を含有しないフラックスを添加することが好ましい。 - 特許庁