recrystallization temperatureとは 意味・読み方・使い方

To provide an antifreeze protein having artificially improved temperature hysteresis and ice recrystallization inhibiting activity.例文帳に追加

温度ヒステリシス、氷の再結晶阻害活性を人工的に向上させた不凍タンパク質を提供する。 - 特許庁

The successive secondary recrystallization annealing or purification annealing is carried out at ≥1,050°C annealing temperature.例文帳に追加

引き続き行われる二次再結晶焼鈍もしくは純化焼鈍は、焼鈍温度1050℃以上で行う。 - 特許庁

Furthermore, the rolling until the temperature in the fillet part becomes not higher than the recrystallization temperature of austenite is performed only by the rolling mill on the upstream side.例文帳に追加

さらには、フィレット部温度がオーステナイトの再結晶温度以下になるまでの圧延を上流側の圧延機のみで行なう。 - 特許庁

In the production method therefor, the steel is hot-rolled so as to be finished at 700°C to a recrystallization temperature Ts, the total draft in the temperature range of the recrystallization temperature Ts or below is controlled to ≥15%, and, after the hot rolling, it is coiled in the temperature range of >500 to <850°C, and is successively subjected to forced cooling.例文帳に追加

その製造方法は、７００℃以上再結晶温度Ｔｓ以下の温度域で熱間圧延を終了し、再結晶温度Ｔｓ以下の温度域での総圧下率を１５％以上とし、熱間圧延後５００℃超８５０℃未満の温度域で巻き取り、続いて強制的に冷却する。 - 特許庁

At this time, since the low temperature heat treatment is performed at a low temperature less than the recrystallization temperature of pure nickel, i.e., at about 600(°C), the mechanical properties of the pure nickel rolling stock are hardly changed.例文帳に追加

このとき、低温熱処理は純ニッケルの再結晶温度以下の低温、すなわち600(℃)程度の温度で施されることから、その機械的性質は殆ど変化しない。 - 特許庁

The recrystallization annealing is performed in a heat treating furnace in a vacuum or inert gas atmosphere, and as the recrystallization annealing condition, the heating temperature is set to 430-750°C and held for 0.5-24 hours.例文帳に追加

再結晶焼鈍は、真空または不活性ガス雰囲気の熱処理炉内で行い、再結晶焼鈍条件は、加熱温度を４３０〜７５０℃に設定し、０．５〜２４時間保持する。 - 特許庁

To provide an anti-freeze protein having high nonfreezing activities such as temperature hysteresis activity, ice recrystallization inhibitory activity, etc.例文帳に追加

温度ヒステリシス活性、氷の再結晶阻害活性等の不凍活性の高い不凍タンパク質を提供する。 - 特許庁

To accelerate recrystallization in subsequent rolling or forging of a steel having a steel composition showing austenitic phase at liquidus temperature by refining the solidification structure of the steel and to reduce manufacturing cost by reducing reduction ratio and forging ratio, lowering recrystallization temperature, and shortening recrystallization time.例文帳に追加

鋼の組成が液相線温度においてオーステナイト相を呈する鋼について、凝固組織を微細化することにより、その後の圧延または鍛造における再結晶を促進し、圧減比や鍛造比の節減、および再結晶温度の低温化、再結晶時間の短時間化による製造コスト削減を図る。 - 特許庁