flame fusion methodとは 意味・読み方・使い方

In the manufacturing method of the mold, spherical molding sand which is manufactured by a flame-fusion method and has ≥SK35 (1770°C) refractoriness, is used as facing sand, and the molding sand except the above spherical molding sand, is used as back sand.例文帳に追加

火炎溶融法にて製造された耐火度ＳＫ３５（１７７０℃）以上の球状鋳物砂を肌砂として使用し、前記球状鋳物砂以外の鋳物砂を裏砂として使用して鋳型を製造する。 - 特許庁

A mold obtained from spherical molding sand made by a flame-fusion method, is heated at the surface temperature of 60-250°C and molten metal is poured to produce the casting having thin portion of ≤6 mm.例文帳に追加

火炎溶融法にて製造された球状鋳物砂より得られる鋳型を表面温度６０℃〜２５０℃に加熱して、溶融金属を注入し、６ｍｍ以下の薄肉部分を有する鋳物を製造する。 - 特許庁

The method of manufacturing the optical fiber coupler includes a diameter reducing stage for making the clad of an optical fiber 11 thin by a flame polishing method and a fusion drawing stage for fusing and drawing at least two optical fibers whose clads are made thin in the diameter reducing stage.例文帳に追加

本発明の光ファイバカプラの製造方法は、光ファイバ１１のクラッドを火炎研磨法により細径化する細径化工程と、細径化工程にてクラッドが細径化された光ファイバ１１を少なくとも２本融着延伸する融着延伸工程とを有する。 - 特許庁

To provide a method for producing a carbon fiber precursor acrylic fiber bundle, by which fusion between single fibers in a flame-resisting step and the deposition of scales originated from silicones in a spinning step and in a baking step can be prevented, and step passableness can be improved.例文帳に追加

耐炎化工程における単繊維間の融着を抑制でき、かつシリコーン由来の紡糸工程、焼成工程でのスケールの堆積を抑制し、工程通過性を改善することができる炭素繊維前駆体アクリル繊維束の製造方法を提供する。 - 特許庁

When the molding sand is regenerated from the mold obtained by using the spherical molding sand made by a flame fusion method as the molding sand, fine powder content in the recovered sand obtained by crushing the mold is set to be ≤0.3 pt.wt. to 100 pts.wt. of the recovered sand.例文帳に追加

鋳物砂として火炎溶融法にて製造された球状鋳物砂を使用して得られた鋳型から鋳物砂を再生する際に、前記鋳型を破砕した回収砂中の微粉分を該回収砂１００重量部に対して０．３重量部以下とする。 - 特許庁

To provide titanium dioxide with high purity and with excellent dispersion properties, having a wide field of industrial application, and having an average diameter within 5-20 μm range especially suitable for a raw material of photocatalyst fine particles and of ceramic moldings in a flame fusion method with which titanium dioxide with the excellent dispersion properties is obtained, and a method for manufacturing the same.例文帳に追加

分散性の良い二酸化チタンが得られる火炎溶融法において、産業的に利用分野の広い、特に光触媒粉体やセラミックス成形体原料として好適な５μｍから２００μｍの範囲の平均径を持つ、高純度で分散性の良い二酸化チタン、及びその製造方法を提供する。 - 特許庁

To provide a treating agent and a method for synthetic fiber for carbon fiber production capable of simultaneously and sufficiently carrying out prevention of fusion of flame-resistant fibers in a flameproofing process and prevention of occurrence of contaminant in a kiln in a carbonization process.例文帳に追加

炭素繊維の製造において、耐炎化工程での耐炎化繊維相互の融着防止と炭素化工程での焼成炉内汚染物質の発生防止とを同時に且つ充分に図ることができる炭素繊維製造用合成繊維処理剤及び炭素繊維製造用合成繊維の処理方法を提供する。 - 特許庁

To 100 pts.wt. of spherical molding sand made by a flame fusion method, a binder composition containing furan resin and a hardener composition having 0-0.7 weight ratio of phosphorus atoms to sulfur atoms represented by [sulfur atom content/(phosphorus atom content + sulfur atom content)] are added in specific ratios, respectively and the mold is made by hardening the above furan resin.例文帳に追加

火炎溶融法で製造された球状鋳物砂１００重量部に対し、フラン樹脂を含有する粘結剤組成物と、［硫黄原子含量／（燐原子含量＋硫黄原子含量）］で示される燐原子と硫黄原子との重量割合が０〜０．７である硬化剤組成物とを、それぞれ特定比率で添加し、前記フラン樹脂を硬化させることにより鋳型を製造する。 - 特許庁